CeO2-Mn2O3 Catalyst:A Potential Pt Replacement for NOx-assisted Soot Oxidation : Presentasi Riset Unggulan Terpadu Internasional




Abstrak
Potensi material-material logam oksida, CeO2 dan Mn2O3, sebagai katalis pengoksidasi materi partikulat (MP) dengan bantuan NOx telah diteliti. Sasaran akhir penelitian ini adalah mendapatkan material pengganti katalis Pt yang digunakan pada system catalytic filter komersial Continuously Regenerating Trapp (CRT). Pengujian aktivitas katalis terhadap reaksi oksidasi gas NO dilakukan dengan menggunakan gas umpan campuran 700 ppm NO, 10% O2, dan argon sebagai gas pembawa. Pada pengukuran aktivitas katalis dalam mengoksidasi MP, reaktor diisi oleh bed MP yang ditempatkan berurutan dengan bed katalis dan dipisahkan oleh wool kwarsa. Katalis yang diuji menunjukan aktivitas yang cukup baik pada oksidasi gas NO walaupun aktivitasnya lebih rendah dari katalis Pt. NO2 yang dihasilkan mencapai kesetimbangan terdinamika pada temperature di atas 620 K. Pada eksperimen oksidasi MP, NO2 yang dihasilkan pada bed pertama memasuki bed MP dan mengoksidasinya. Eksperimen secara isothermal pada temperature 625 K menunjukkan bahwa aktivitas katalis yang dibuat setara dengan katalis rujukan Pt. Gejala ini dapat dijelaskan sebagai berikut. Pada temperature 625 K dan temperature di atasnya, kedua jenis katalis telah menghasilkan NO2 yang konsentrasinya mencapai kurva kesetimbangan termodinamika, sehingga jumlah NO2 yang dihasilkan relative sama. Dengan demikian aktivitas katalis dalam mengoksidasi MP dengan bantuan NOx juga relative sama, sehingga katalis CeO2-Mn2O3 sangat berpotensi sebagai pengganti katalis Pt pada system CRT.

Kata Kunci: System katalitik konverter, oksidasi Materi Partikulat, Oksidasi NO, Pt, CeO2, Mn2O3

Abstract
Non-noble metal materials based on CeO2 and Mn2O3 have been studied in order to evaluate their potential as NOx-assisted soot oxidation catalysts. The final objective is to find a cheap material as substitute for Pt catalyst, normally applied in Continuously Regenerating Trapp (CRT), a commercial soot catalytic conversion system. The catalytic activities were tested in flow reactor equipment both for NO oxidation and NOx-assisted soot oxidation. In testing the performance as NO oxidation catalyst, the reactor was filled only with catalyst. The feed gas used was 700 ppm NO, 10% O2 and Argon as gas balance. In the investigation on the activity of the NOx assisted soot oxidation catalyst the reactor was filled with soot bed placed downstream of the catalyst bed. Similar experiments were carried out with commercial Pt catalyst for comparison.
The catalysts were found to be significantly active in the oxidation of NO but the activity was lower than that of the commercial Pt catalyst. Produced NO2 reaches thermodynamic equilibrium at 620 K and above. In NOx-assisted soot oxidation experiment, NO2, generated in the first bed enters the soot bed in which NO2-soot reaction takes place. Isothermal experiment at 625 K showed that the reaction rate is comparable with that of Pt catalyst. It is generally accepted that the NOx-assisted soot oxidation rate is mainly influenced by the amount of NO2. Since at 625 K, both with our catalyst and the commercial Pt catalyst, the amount of NO2 has reached equilibrium, it should be logical that the oxidation rates of the two catalysts are comparable. Therefore, the CeO2-Mn2O3 based catalyst is a potential Pt replacement to be used in the CRT’s NOx-assisted soot oxidation catalyst.

Key words: Catalytic Conversion System, soot oxidation, NO oxidation, Pt, CeO2, Mn2O3,

Entry Oleh Ahmad


Ketersediaan

Tidak ada salinan data


Informasi Detil

Judul Seri
-
No. Panggil
-
Penerbit Riset Unggulan Terpadu Internasiol : Jakarta..,
Deskripsi Fisik
-
Bahasa
English
ISBN/ISSN
-
Klasifikasi
NONE
Tipe Isi
-
Tipe Media
-
Tipe Pembawa
-
Edisi
-
Subyek
Info Detil Spesifik
-
Pernyataan Tanggungjawab

Versi lain/terkait

Tidak tersedia versi lain


Lampiran Berkas



Informasi


DETAIL CANTUMAN


Kembali ke sebelumnyaXML DetailCite this